單/雙面紫銅鋼復合板帶
Single/double-side copper-steel composite plates&strips(steel as base)
特性優點
Character
銅及銅合金復合鋼帶具有高強度、高導熱性、高導電性、良好的可塑性、良好的耐磨性能、美觀的外表以及良好的再加工性(上釉或鍍鉻)，這一類材料均可雙面復合亦可單面復合，并用于所有電鍍件性能不足以滿足其他要求、純有色金屬花費昂貴或不具備良好加工性能的領域。
Copper and copper alloy clad steel has high strength, high thermal conductivity, high conductivity, good plasticity and wear-resisting property , beautiful appearance and good reprocess -ability(Glazing or chrome plating).This kind of material can clad one side or both sides and be used for fields that all plating items can not satisfy the requirement ,pure non—ferrous metal is expensive and without good processability．
通常可供規格范圍
Specifications available
復層厚度比例可以依據客戶要求不限于3~15% ; 雙面銅層可以相同也可以不同(依據客戶的要求調整)
The thickness of the copper is not limited 3%~15% ; but custom’ requirement . One side of the copper can be different from the other.
產品性能
Product performance
Single/double-side copper-steel composite plates&strips(steel as base)
特性優點
Character
銅及銅合金復合鋼帶具有高強度、高導熱性、高導電性、良好的可塑性、良好的耐磨性能、美觀的外表以及良好的再加工性(上釉或鍍鉻)，這一類材料均可雙面復合亦可單面復合，并用于所有電鍍件性能不足以滿足其他要求、純有色金屬花費昂貴或不具備良好加工性能的領域。
Copper and copper alloy clad steel has high strength, high thermal conductivity, high conductivity, good plasticity and wear-resisting property , beautiful appearance and good reprocess -ability(Glazing or chrome plating).This kind of material can clad one side or both sides and be used for fields that all plating items can not satisfy the requirement ,pure non—ferrous metal is expensive and without good processability．
通常可供規格范圍
Specifications available
| 標準尺寸 | 銅-鋼 | 銅-鋼-銅 |
| 帶材寬度 | < 800 mm | < 800 mm |
| 帶材厚度 | 0,05- 3,0 mm | 0,05 - 3,0 mm |
| 覆層厚度 | 3 - 15 % | 3 - 15 % |
| 芯層/基層材料 | Carbon steel | Carbon steel |
| 覆層材料 | Cu | Cu |
| 交付形式 | 卷材 | 卷材 |
| 表面處理狀態 | 亮面 | 亮面 |
復層厚度比例可以依據客戶要求不限于3~15% ; 雙面銅層可以相同也可以不同(依據客戶的要求調整)
The thickness of the copper is not limited 3%~15% ; but custom’ requirement . One side of the copper can be different from the other.
產品性能
Product performance
|
材料 Material |
成分Composition（%） |
密度 Density (g/cm³) |
導電率 Conductivity (m/Ωmm2) |
抗拉強度（Mpa） Tensile Strength（Mpa） |
延伸率（%） Elongation（%） |
復合強度 Combined Strength |
|||
|
退火軟態 Annealing |
半硬態Half hard state | ||||||||
| 退火態Annealing | 半硬態Half hard state | ||||||||
|
紫銅復鋼 Copper clad steel |
5/90/5 | 7.9 | 12.7 | ≥265 | ≥365 | ≥37 | ≥15 |
反復彎曲 試驗斷裂 后不分層 Re-bend until break without separation |
|
|
紫銅復鋼 Copper clad steel |
10/80/10 | 8.0 | 17.8 | ≥250 | ≥350 | ≥40 | ≥20 | ||